Highly flexible gel glue, recommended for marble and natural stone, produced in the form of a dry mix and the highest quality cement binder, aggregates and specially selected natural and synthetic modifying agents.

Features

• type C2TE
• for all types of tiles, including ceramic, porcelain and glass
• recommended for marble and natural stone
• on difficult surfaces, e.g. old tiles, terrazzo, plasterboards, waterproofing
• for balconies, terraces, underfloor heating
• no runoff even with large formats
• very good flow under the plate
• for walls and floors
• thickness 2-15 mm
• frost-resistant
• waterproof
• for high temperature operation
• consistency adjusted to the needs
• inwards and outwards

Application

• types of glued claddings: tiles, terracotta, porcelain stoneware, discoloration-prone marble / natural stone cladding, non-discolouring marble / natural stone cladding, clinker, stoneware, ceramic mosaic, glass mosaic, glass tiles, concrete / cement mortar tiles
• the formats of the glued element in small, medium and large format tiles (≤ 0.25 m) and the length of the longer side ≤ 100 cm
• types of objects in: residential construction + public utility facilities, educational, office, health care + commercial and service construction + religious buildings
• installation site: areas with low traffic, areas with medium traffic, rooms with low operational loads in all types of facilities, kitchen, bathroom, laundry room, terraces, balconies, loggias, external slab stairs, showers, car washes, rooms washed with plenty of water
• standard substrates: cement floors and screeds, anhydrite screeds, cement and cement-lime plasters, gypsum plasters, cellular concrete masonry, silicate brick or hollow brick, brick or ceramic block, gypsum block wall
• deformable substrates or the so-called difficult: concrete, terrazzo, mineral, dispersion and reactive sealing coats, dry screeds made of gypsum boards, floor screeds (cement or anhydrite) with immersed heating, water or electric, floor screeds with a heating mat embedded in glue, plasters with concealed heating, boards plasterboard, gypsum fiber boards, cement fiber boards, existing ceramic or stone cladding (tile to tile) only inside, resin varnishes for concrete bonded to the substrate, dispersion, oil paint coatings bonded to the substrate, OSB / 3 boards , OSB / 4 boards and chippings on the floor (thickness> 25 mm), OSB / 3 boards, OSB / 4 boards and chippings on the wall (thickness> 18 mm)

Technical data

• a bulk density of about 1.4 g / cm
• mixing ratio (water / dry mix) 0.26-0.33 l / 1 kg, 1.3-1.65 l / 5 kg, 5.85-7.43 l / 22.5 kg, 6.5- 8.25 l / 25 kg
• minimum / maximum adhesive thickness 2-15 mm
• adhesive preparation temperature, substrate and ambient temperature during work from +5 C to +35 C
• maturing time 5 min
• lifetime (standby time) * approx. 4 h
• open time * minimum 30 min
• correctability * 20 min
• stepping on the floor / pointing * after 12 h
• full operational loads - pedestrian traffic * after 3 days
• full operational loads - road traffic * after 14 days
• underfloor heating (heated surfaces) * after 14 days
• reaction to fire A1 / A1f
• joint strength expressed as initial adhesion ≥ 1.0 N / mm
• joint durability under conditioning / thermal aging conditions expressed as adhesion after thermal aging ≥ 1.0 N / mm
• durability of the joint under water / moisture conditions, expressed as adhesion after immersion in water ≥ 1.0 N / mm
• joint durability under freeze-thaw cycles expressed as adhesion after freeze-thaw cycles ≥ 1.0 N / mm
• consumption for 30x30 cm tiles from 2.0 kg / m ²

* times given in the table are recommended for application conditions at a temperature of about 23 C and 55% humidity