Polyurethane adhesive used for gluing polystyrene boards when insulating external walls of buildings using the ETICS (BSO) method, gluing cassettes in polystyrene, wall panels, as well as for installing window sills. The product also fills gaps in thermal insulation.

Features

• one-component
• low pressure
• easy and convenient to use
• enables quick execution of works (initial hardening after 2 hours, full hardening after only 24 hours *)
• very efficient (average yield about 8 m ² per can)
• very good adhesion to all mineral substrates
• shows excellent adhesion to concrete, ceramic, wooden and PVC substrates as well as all types of polystyrene and plaster in
• used in a wide range of temperatures, especially recommended in cold periods in autumn and spring

Technical data

• working temperature (substrate and environment) from +0 C to +30 C
• can temperature from +10 C to +25 C
• correction time up to about 10 minutes *
• dowel time after approx. 2 h
• full hardening time after 24 hours
• storage temperature from +5 C to +35 C
• apparent density 10% 15 kg / m ³
• dimension change in linear after 48 h at +70 C and 90% relative humidity: length and width ≤ 2%, thickness ≤ 1%
• compressive stress at 10% relative deformation of free foam adhesive ≥ 40
• tensile strength perpendicular to the surface, polystyrene / concrete joint ≥ 0.08 MPa
• tensile strength perpendicular to the surface, XPS / concrete joint ≥ 0.08 MPa
• foam adhesion in air-dry state: to concrete ≥ 0.25 MPa; for polystyrene ≥ 0.08 MPa; up to XPS ≥ 0.15 MPa; for concrete with bituminous coating ≥ 0.15 MPa
• consumption about 8 m ² from the can
• Technical Approval ITB AT-15-8153 / 2014 with an annex
• 750 ml package (can)

* all the mentioned parameters refer to the temperature of +23 C and 55% of the relative air humidity; higher temperatures and higher air humidity accelerate, and lower temperatures and lower air humidity slow down the processing time and the course of hardening