Universal mineral joint for joints 2-20 mm with very low content of chemical additives. Protects against discoloration and eliminates efflorescence. Very long machinability with accelerated cleaning ability.

properties

• ekokompatybilna
• does not thicken (constant workability up to 30 min)
• does not collapse (full joint filling)
• full grout (ixotropic, holds shape)
• quick and easy application (extended plasticity under the trowel)
• quick washing (waiting time for finishing 10 min)
• uniform color (selected and stable raw materials)
• abrasion resistance (the purest mineral aggregates)
• early foot traffic (commissioning after 8 hours)
• compact and smooth surface (homogeneous and granular mix)
• insensitive to aggressive waters (very low content of chemical additives)

Technical data

• EC 1-R plus GEV-Emicode compliance (GEV 6744 / 11.01.02 certified)
• flexural strength after 28 days ≥ 10 N / mm ² (according to EN 12808-3)
• compressive strength after 24 h ≥ 15 N / mm ² (according to ISO 13007-4.1.4)
• compressive strength after 28 days ≥ 40 N / mm ² (according to ISO 13007-4.1.4)
• strength after freeze-thaw cycles: bending ≥ 5 N / mm ² , compression ≥ 40 N / mm ² - according to EN 12808-3
• abrasion resistance after 28 days ≤ 300 mm ³ (according to EN 12808-2)
• water absorption after 30 min ≤ 0.8 g (according to EN 12808-5)
• water absorption after 240 min ≤ 1.8 g (according to EN 12808-5)
• operating temperature from -40 C to +90 C
• CG2 WA compliance (according to ISO 13007-3)

Note: Data obtained at a temperature of +23 C, relative humidity 50% depending on the conditions prevailing at the construction site and ventilation.

Application

• in and out
• street furniture
• floors and walls
• residential, commercial and industrial buildings
• heavily loaded surfaces
• zones exposed to temperature jumps and freezing
• swimming pools, troughs, fountains