Air-oxygen-curing 3-20 mm joint mortar, based on synthetic resin, for lightly loaded paving, ceramic and stone coverings, especially for porcelain stoneware tiles with a thickness of ≥ 2 cm on a set and unbound substructure.

Features

• one-component
• ready to use
• optimal water permeability
• possibility of building in during light rainfall
• resistant to mr z / sl used for deicing
• for joint widths from 3 mm
• slime consistency, easy to apply
• drainage properties
• provides a uniform appearance to the cladding
• no lichen in the plant
• waterproof
• frost-resistant
• outside

Application

• grouting paving, natural stone, ceramic, clinker cladding, and especially porcelain terrace tiles with a thickness of ≥ 2 cm in external areas on a bound and unbound substructure
• pointing of untreated, high-quality concrete slabs
• for applications in lightly loaded areas, such as building entrance areas, terraces, paths and garden areas

Technical data

• mixing ratio ready to use
• application time approx. 45 minutes at +20 ° C
• can be walked on after about 24 hours at a temperature of +20 C (protect the freshly grouted surface)
• fully loaded after about 7 days
• bending strength of about 6 N / mm ²
• compressive strength approx. 15 N / mm ²
• water permeability 1.7 x 10 ^-5 m / s (with a 5% share of the grout about 3 l / m ² / h)
• joint width / depth from 3 mm to a maximum of 20 mm / at least 30 mm (for paving stones); from 15 mm / at least double the joint width; the depth of the joint when replacing the joints of the paving stone, minimum 2/3 of the height of the stone
• application temperature from +3 C to +25 C.
• consumption from 0.6 kg / m ² to 27.9 kg / m ²
• 18-month storage
• package 25 kg