For making very fast setting and drying primers in floors:
- connected with concrete base, cement screeds, etc. - laying thickness 10 - 100 mm,
- on insulation made of foil, roofing felt, foamed polystyrene, mineral wool, etc. - laying thickness 35 - 100 mm,
- with water heating - laying thickness 60 - 80 mm (including at least 35 mm above the heating cables).
- for applying pressure layers on terraces, balconies, roofs, etc. - allows you to lay tiles after 24 hours.
- for making cement floors in boiler rooms, basements, individual garages, utility rooms, etc.
- for use in flats, offices, hospitals, schools, shops, cinemas, etc. public facilities.

Technical data:
- packaging: 25 kg,
- pallet: 1050 kg,
- product in accordance with: PN-EN 13813,
- reaction to fire: A1fl,
- evolution of corrosive substances: cement mortar (CT),
- compressive strength: above 30 N / mm2 (C30),
- flexural strength: above 5 N / mm2 (F%),
- mixing ratio: 2.2 - 2.7 l of water per 25 kg,
- amount of ready-mixed mortar: 1 m3 with about 2000 kg of dry mix with 10% water,
- consumption time: approx. 0.5 h *,
- layer thickness: bound underlays: 10 - 100 mm, underlays on insulation: 40 - 80 mm, underlays in heating systems: 60 - 80 mm (including at least 35 mm above heating cables),
- material consumption: approx. 2.0 kg / m2 for each mm of thickness,
- laying speed: approx. 20 m2 / h,
- application temperature: from +10 C to +30 C,
- curing time: for pedestrian traffic: approx. 8 h *,
- floor laying: after a minimum of 24 hours * (for ceramic tiles).

* At +20 C and 65% relative humidity. Higher temperature and lower humidity shorten the time, lower temperature and higher humidity lengthen the given time.