Factory prepared, dry mix based on the highest quality mineral binders, an additional and modifier, as well as quartz and trass fillers.

Features

• contains lime, a natural binder, for a century the building material used in production - the lime content determines the flexibility and resistance of the layer to cracking
• high resistance to microcracks - thanks to the content of special microfibers, which additionally strengthen the structure of the material
• very fine graining (aggregate up to 0.2 mm) - allows for a very smooth surface
• wide scope of application - the putty is easy to apply in both 1 mm and 10 mm thick layers
• white color of the plaster allowing for easy and economical covering of the surface with paint
• thanks to a specially selected recipe, it perfectly cooperates with historical mortars used for erecting the object undergoing renovation

Application

• making the final finishing layer on surfaces made of concrete, cement and cement-lime plaster, renovation plaster
• on wall surfaces and ceiling v
• inside and outside the building in

Technical data

• water / dry mix mixing ratio 7-8 l / 25 kg
• mortar preparation temperature, substrate and ambient temperature during work from +5 C to +25 C
• time of the mortar's readiness to work approx. 2 h
• open working time approx. 25 min
• minimum layer thickness 1 mm
• maximum layer thickness 10 mm
• reaction to fire A1
• water absorption W _C 1
• water vapor permeability μ ≤15
• adhesion 0.3 N / mm - FP: B
• meets the requirements of PN-EN 998-1: 2016
• average consumption of about 1.5 kg of mortar per 1 m ² , with a layer thickness of 1 mm
• package 25 kg