Acid-resistant mortar based on epoxy resin, selected quartz sand and special additives, with a smooth surface and shiny colors, used to fill joints with a width of 2 to 20 mm. Perfect for surfaces where perfect cleanliness is required.

Features

• two-component
• optimal machinability
• ease of use
• non-absorbent
• very easy to clean
• she was sobbing
• non-marking
• high hardness
• good chemical resistance

Application

• pointing of floors with high traffic loads, in industrial warehouses, shopping centers, etc.
• pointing in swimming pools, also those filled with sea water
• as an adhesive mortar (R2T class in accordance with PN-EN 12004) for bonding metal and glass-fiber reinforced laminate substrates
• grouting ceramic or stone tiles on floors and walls, such as glazed or marble mosaics, porcelain, clinker, in areas exposed to acid in or in areas where non-absorbent joints are required, such as industrial kitchens, tanneries, dairies, paper mills, laboratory tables, slaughterhouses

Note: Before grouting the stone tiles, check the compatibility of the mortar with the given type of stone (possibility of cleaning, possible color change of the stone).

Technical data

• color / form: component A thick colored paste; component B viscous liquid
• chemical base epoxy resin, selected aggregates, additives
• the density of the mixture ~ 1.65 kg / dm ³
• joint width from 2 to 20 mm
• Shelf life after mixing ~ 45 minutes (at +23 C / 50% relative humidity)
• thermal resistance of at least -20 C; maximum +100 C.
• abrasion resistance 160 mm ³ (according to PN-EN 12808-2)
• bending strength after storage in dry conditions 38 MPa (according to PN-EN 12808-3)
• compressive strength after storage in dry conditions 58 MPa (according to PN-EN 12808-3)
• shrinkage 0.8 mm (according to PN ‐ EN 12808‐4)
• water absorption after 240 min 0.05 g (according to PN-EN 12808-5)
• application conditions substrate and ambient temperature min. +10 C / max. +30 C
• storage conditions product stored in original, undamaged packaging, protected against frost and at temperatures not higher than +35 C, preferably use within 24 months from the production date
• package 5 kg